Zytel 101L
PA66 Zytel 101L NC010中英文物性参数物性表
以下是PA66 Zytel 101L NC010中英文物性表
DuPont Zytel® 101L NC010 Nylon 66
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Specific Gravity比重
1.14 g/cc
1.14 g/cc
DAM; ASTM D792
Water Absorption吸水率
1.2 %
@Temperature 23.0 °C
1.2 %
@Temperature 73.4 °F
Immersion 24h; DAM; ASTM D570
8.5 %
@Temperature 23.0 °C
8.5 %
@Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage线性收缩率
0.015 cm/cm
@Thickness 3.20 mm
0.015 in/in
@Thickness 0.126 in
Flow; DAM
Linear Mold Shrinkage, Flow 线性收缩率/流动
0.014 cm/cm
@Thickness 2.00 mm
0.014 in/in
@Thickness 0.0787 in
Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse线性收缩率/横向
0.014 cm/cm
@Thickness 2.00 mm
0.014 in/in
@Thickness 0.0787 in
Normal; DAM; ISO 294-4
Mechanical Properties力学性能
Hardness, Rockwell M罗氏硬度M
59
59
50%RH; ASTM D785
79
79
DAM; ISO 2039/2
Hardness, Rockwell R罗氏硬度R
108
108
50%RH; ASTM D785
121
121
DAM; ISO 2039/2
Tensile Strength拉伸强度
38.0 MPa
@Temperature 121 °C
5510 psi
@Temperature 250 °F
50%RH; ASTM D638
41.0 MPa
@Temperature 77.0 °C
5950 psi
@Temperature 171 °F
114 MPa
@Temperature -40.0 °C
16500 psi
@Temperature -40.0 °F
DAM; ASTM D638
Tensile Stress拉伸应力
0.000 MPa
@Strain 0.000 %,
Temperature -40.0 °C
0.000 psi
@Strain 0.000 %,
Temperature -40.0 °F
DAM; ISO 527
10.39 MPa
@Strain 0.390 %,
Temperature 40.0 °C
1507 psi
@Strain 0.390 %,
Temperature 104 °F
89.52 MPa
@Strain 3.43 %,
Temperature 0.000 °C
12980 psi
@Strain 3.43 %,
Temperature 32.0 °F
98.47 MPa
@Strain 4.89 %,
Temperature 0.000 °C
14280 psi
@Strain 4.89 %,
Temperature 32.0 °F
DAM; ISO 527
PA6和PA66的区别:
PA6的化学物理特性和PA66很相似，然而，它的熔点较低，而且工艺温度范围很宽。
它的抗冲击性和抗溶解性比PA66要好,但吸湿性也更强。因为塑件的许多品质特性
都要受到吸湿性的影响，因此使用PA6设计产品时要充分考虑到这一点。为了提高
PA6的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了
提高抗冲击性还加入合成橡胶，如EPDM和SBR等。
对于没有添加剂的产品，PA6的收缩率在1%到1.5%之间。加入玻璃纤维添加剂可以使
收缩率降低到0.3%（但和流程相垂直的方向还要稍高一些）。成型组装的收缩率主要
受材料结晶度和吸湿性影响。